Dmax cubeX²® ML – Super translucent (Multilayer)

Based on the “Dmax cubeX²® – cubic zirconia system®” the blanks offer a flowing color gradation from cervical to incisal. The manufacture of aesthetic monoliths has never been this efficient before. The lively chroma and an increase of translucency in the incisal third meet the highest demands of modern CAD materials.

  • individual color gradients – which would otherwise only be possible with the extensive color-brush technique
  • High color reliability – due to the Multi Additive Technology®
  • Resistant to wrapping during sintering – due to individual isostatic redensification of each blank
5Y-TZP
>800 MPa
8 VITA® shades

 

Dmax cubeX²® ML for open systems Ø 98,5 mm

 

Art. no. VITA® color Height (mm)
G852007 A1 14
G854007 A1 18
G856007 A1 22
G852001 A2 14
G854001 A2 18
G856001 A2 22
G852002 A3 14
G854002 A3 18
G856002 A3 22
G852003 A3,5 14
G854003 A3,5 18
G856003 A3,5 22
G852008 B1 14
G854008 B1 18
G856008 B1 22
G852004 B2 14
G854004 B2 18
G856004 B2 22
G852005 C2 14
G854005 C2 18
G856005 C2 22
G852006 D3 14
G854006 D3 18
G856006 D3 22

Indications

Veneers
Inlays/Onlays
Reduzierte Krone
Monolithische Krone Frontzahn
Monolithische Krone Seitenzahn
Hybrid Abutment Krone
Monolithische Brücke (3-gliedrig)
Reduzierte Brücke (3-gliedrig)
Manual / Gebrauchsanleitung

Consult instructions for use

Pre-colored blanks are nor allowed to be used with patented coloring technologies.

Physical specifications

Characteristics Unit Value
Density (after sintering) [g/cm³] > 6,0
CTE (25 – 500°C) [10⁻⁶ K⁻¹] 10
Fracture toughness (SEVNB) [MPa√m] > 4,7
Fracture toughness (SEPB) [MPa√m] 2,4
Flexural strength [MPa] ≥ 800
E-Modulus [GPa] > 210

Chemical composition

ZrO² + HfO² ≥ 90
Y²O³ < 10
Al²O³ < 0,01
Other oxides < 0,15